Pressure Dependence of ZnDTP Tribochemical Film Formation: A Combinatorial Approach

Heuberger, Roman ; Rossi, Antonella ; Spencer, Nicholas

In: Tribology Letters, 2007, vol. 28, no. 2, p. 209-222

Zum persönliche Liste hinzufügen
    Titel
    • Pressure Dependence of ZnDTP Tribochemical Film Formation: A Combinatorial Approach
    Autor
    • Heuberger, Roman. Laboratory for Surface Science and Technology, Department of Materials, ETH Zurich, Wolfgang-Pauli-Strasse 10, 8093, Zurich, Switzerland
    • Rossi, Antonella. Laboratory for Surface Science and Technology, Department of Materials, ETH Zurich, Wolfgang-Pauli-Strasse 10, 8093, Zurich, Switzerland
    • Spencer, Nicholas. Laboratory for Surface Science and Technology, Department of Materials, ETH Zurich, Wolfgang-Pauli-Strasse 10, 8093, Zurich, Switzerland
    Dokumententyp
    • Postprint
    Sprache
    • Englisch
    Veröffentlicht in
    • Tribology Letters, 2007, vol. 28, no. 2, p. 209-222. Springer US; http://www.springer-ny.com
    Andere elektronische Ausgabe
    OAI-PMH-ID
    • oai:doc.rero.ch:314307
    Summary
    Combinatorial testing has been performed on zinc dialkyldithiophosphate (ZnDTP)-containing lubricants, to investigate the effects of contact pressure on the formation of tribochemical films. Contact pressures ranging from 25 to 500MPa were applied in ball-on-disc tribotests with oscillating load. Both the ball and the disc were investigated by means of small-area and imaging X-ray photoelectron spectroscopy (XPS). The thickness and the composition of the reaction layer were estimated from the XPS data. The thickness of the reaction layer in the tribologically stressed areas of the ball and of the disc increased with both temperature and contact pressure. The reaction layer mainly consisted of short-chain poly(thio)phosphates, shorter chains being observed at higher contact pressures. At high pressures, the presence of a thick, high-toughness short-chain poly(thio)phosphate layer can explain the lower friction and dimensional wear coefficients observed. On the ball, similar anti-wear film formation mechanisms were observed as on the disc, zinc sulphide being deposited in the post-contact region