Flame spray synthesis and characterisation of stabilised ZrO2 and CeO2 electrolyte nanopowders for SOFC applications at intermediate temperatures

Heel, Andre ; Vital, Andri ; Holtappels, Peter ; Graule, Thomas

In: Journal of Electroceramics, 2009, vol. 22, no. 1-3, p. 40-46

Add to personal list
    Title
    • Flame spray synthesis and characterisation of stabilised ZrO2 and CeO2 electrolyte nanopowders for SOFC applications at intermediate temperatures
    Author
    • Heel, Andre. Laboratory for High Performance Ceramics, EMPA Swiss Federal Laboratories for Materials Testing and Research, Ueberlandstrasse 129, 8600, Duebendorf, Switzerland
    • Vital, Andri. Laboratory for High Performance Ceramics, EMPA Swiss Federal Laboratories for Materials Testing and Research, Ueberlandstrasse 129, 8600, Duebendorf, Switzerland
    • Holtappels, Peter. Laboratory for High Performance Ceramics, EMPA Swiss Federal Laboratories for Materials Testing and Research, Ueberlandstrasse 129, 8600, Duebendorf, Switzerland
    • Graule, Thomas. Laboratory for High Performance Ceramics, EMPA Swiss Federal Laboratories for Materials Testing and Research, Ueberlandstrasse 129, 8600, Duebendorf, Switzerland
    Document Type
    • Postprint
    Language
    • English
    Published in
    • Journal of Electroceramics, 2009, vol. 22, no. 1-3, p. 40-46. Springer US; http://www.springer-ny.com
    Other Version
    OAI-PMH Identifier
    • oai:doc.rero.ch:311360
    Summary
    Zirconia (Y0.16Zr0.84O2, Sc0.2Zr0.8O2 and Sc0.2Ce0.01Zr0.79O2) and ceria (Gd0.2Ce0.8O2) based electrolyte materials are synthesised at production rates up to 260g h−1 by a liquid-fed one-step flame spray synthesis from water-based solutions, or cost-effective rare earth nitrates with a high water content. It was found that this one-step synthesis, based on an acetylene-supported flame is able to produce phase pure and highly crystalline, nanoscale electrolyte materials. The as-synthesised powders show a cubic lattice structure independent of production rates. Specific surface areas of the powders were adjusted between 20 and 60m2 g−2, where the latter is an upper limit for the further processing of the powders in terms of screen printing. The influence of process parameters on morphology, particle size, composition, crystallinity, lattice parameter, shrinkage behaviour and coefficient of thermal expansion of the as-synthesised powders were systematically investigated by transmission electron microscopy (TEM), nitrogen adsorption (BET), X-ray diffraction (XRD) and dilatometry. Electrochemical impedance spectroscopy (EIS) was applied at temperatures between 300°C and 900°C and confirmed the high quality and the competitive electrochemical behaviour of the produced powders